Titanium phosphate glass microspheres for bone tissue engineering

We have demonstrated the successful production of titanium phosphate glass microspheres in the size range of ~10-200 µm using an inexpensive, efficient, easily scalable process and assessed their use in bone tissue engineering applications. Glasses of the following compositions were prepared by melt-quench techniques: 0.5P2O5-0.4CaO-(0.1 - x)Na2O-xTiO2, where x = 0.03, 0.05 and 0.07 mol fraction (denoted as Ti3, Ti5 and Ti7 respectively). Several characterization studies such as differential thermal analysis, degradation (performed using a novel time lapse imaging technique) and pH and ion release measurements revealed significant densification of the glass structure with increased incorporation of TiO2 in the glass from 3 to 5 mol.%, although further TiO2 incorporation up to 7 mol.% did not affect the glass structure to the same extent. Cell culture studies performed using MG63 cells over a 7-day period clearly showed the ability of the microspheres to provide a stable surface for cell attachment, growth and proliferation. Taken together, the results confirm that 5 mol.% TiO2 glass microspheres, on account of their relative ease of preparation and favourable biocompatibility, are worthy candidates for use as substrate materials in bone tissue engineering applications.

Bone marrow-derived mesenchymal stem cells become anti-angiogenic when chondrogenically or osteogenically differentiated:implications for bone and cartilage tissue engineering

Osteochondral tissue repair requires formation of vascularized bone and avascular cartilage. Mesenchymal stem cells stimulate angiogenesis both in vitro and in vivo but it is not known if these proangiogenic properties change as a result of chondrogenic or osteogenic differentiation. We investigated the angiogenic/antiangiogenic properties of equine bone marrow-derived mesenchymal stem cells (eBMSCs) before and after differentiation in vitro. Conditioned media from chondrogenic and osteogenic cell pellets and undifferentiated cells was applied to endothelial tube formation assays using Matrigel™. Additionally, the cell secretome was analysed using LC-MS/MS mass spectrometry and screened for angiogenesis and neurogenesis-related factors using protein arrays. Endothelial tube-like formation was supported by conditioned media from undifferentiated eBMSCs. Conversely, chondrogenic and osteogenic conditioned media was antiangiogenic as shown by significantly decreased length of endothelial tube-like structures and degree of branching compared to controls. Undifferentiated cells produced higher levels of angiogenesis-related proteins compared to chondrogenic and osteogenic pellets. In summary, eBMSCs produce an array of angiogenesis-related proteins and support angiogenesis in vitro via a paracrine mechanism. However, when these cells are differentiated chondrogenically or osteogenically, they produce a soluble factor(s) that inhibits angiogenesis. With respect to osteochondral tissue engineering, this may be beneficial for avascular articular cartilage formation but unfavourable for bone formation where a vascularized tissue is desired. © Copyright 2014, Mary Ann Liebert, Inc.

An initial evaluation of gellan gum as a material for tissue engineering applications

Alpha-modified minimum essential medium (αMEM) has been found to cross-link a 1% gellan gum solution, resulting in the formation of a self-supporting hydrogel in 1:1 and 5:1 ratios of polysaccharide: αMEM. Rheological data from temperature sweeps confirm that in addition to orders of magnitude differences in G' between 1% gellan and 1% gellan with αMEM, there is also a 20°C increase in the temperature at which the onset of gelation takes place when αMEM is present. Frequency sweeps confirm the formation of a true gel; mechanical spectra for mixtures of gellan and αMEM clearly demonstrate G' to be independent of frequency. It is possible to immobilize cells within a three-dimensional (3D) gellan matrix that remain viable for up to 21 days in culture by adding a suspension of rat bone marrow cells (rBMC) in αMEM to 1% gellan solution. This extremely simple approach to cell immobilization within 3D constructs, made possible by the fact that gellan solutions cross-link in the presence of millimolar concentrations of cations, poses a very low risk to a cell population immobilized within a gellan matrix and thus indicates the potential of gellan for use as a tissue engineering scaffold. © 2007 Sage Publications.

Gravity spun polycaprolactone fibers for applications in vascular tissue engineering:proliferation and function of human vascular endothelial cells

Poly(ε-caprolactone) (PCL) fibers produced by wet spinning from solutions in acetone under low-shear (gravity-flow) conditions resulted in fiber strength of 8 MPa and stiffness of 0.08 Gpa. Cold drawing to an extension of 500% resulted in an increase in fiber strength to 43 MPa and stiffness to 0.3 GPa. The growth rate of human umbilical vein endothelial cells (HUVECs) (seeded at a density of 5 × 104 cells/mL) on as-spun fibers was consistently lower than that measured on tissue culture plastic (TCP) beyond day 2. Cell proliferation was similar on gelatin-coated fibers and TCP over 7 days and higher by a factor of 1.9 on 500% cold-drawn PCL fibers relative to TCP up to 4 days. Cell growth on PCL fibers exceeded that on Dacron monofilament by at least a factor of 3.7 at 9 days. Scanning electron microscopy revealed formation of a cell layer on samples of cold-drawn and gelatin-coated fibers after 24 hours in culture. Similar levels of ICAM-1 expression by HUVECs attached to PCL fibers and TCP were measured using RT-PCR and flow cytometry, indicative of low levels of immune activation. Retention of a specific function of HUVECs attached to PCL fibers was demonstrated by measuring their immune response to lipopolysaccharide. Levels of ICAM-1 expression increased by approximately 11% in cells attached to PCL fibers and TCP. The high fiber compliance, favorable endothelial cell proliferation rates, and retention of an important immune response of attached HUVECS support the use of gravity spun PCL fibers for three-dimensional scaffold production in vascular tissue engineering. © Mary Ann Liebert, Inc.

Novel biodegradable fibres for applications in tissue engineering and drug delivery

The preparation and characterisation of novel biodegradable polymer fibres for application in tissue engineering and drug delivery are reported. Poly(e-caprolactone) (PCL) fibres were produced by wet spinning from solutions in acetone under low shear (gravity flow) conditions. The tensile strength and stiffness of as-spun fibres were highly dependent on the concentration of the spinning solution. Use of a 6% w/v solution resulted in fibres having strength and stiffness of 1.8 MPa and 0.01 GPa respectively, whereas these values increased to 9.9 MPa and 0.1 GPa when fibres were produced from 20% w/v solutions. Cold drawing to an extension of 500% resulted in further increases in fibre strength (up to 50 MPa) and stiffness (0.3 GPa). Hot drawing to 500% further increased the fibre strength (up to 81 MPa) and stiffness (0.5 GPa). The surface morphology of as-spun fibres was modified, to yield a directional grooved pattern by drying in contact with a mandrel having a machined topography characterised by a peak-peak separation of 91 mm and a peak height of 30 mm. Differential scanning calorimetery (DSC) analysis of as-spun fibres revealed the characteristic melting point of PCL at around 58°C and a % crystallinity of approximately 60%. The biocompatibility of as-spun fibres was assessed using cell culture. The number of attached 3T3 Swiss mouse fibroblasts, C2C12 mouse myoblasts and human umbilical vein endothelial cells (HUVECs) on as-spun, 500% cold drawn, and gelatin coated PCL fibres were observed. The results showed that the fibres promoted cell proliferation for 9 days in cell culture and was slightly lower than on tissue culture plastic. The morphology of all cell lines was assessed on the various PCL fibres using scanning electron microscopy. The cell function of HUVECs growing on the as-spun PCL fibres was evaluated. The ability HUVECs to induce an immune response when stimulated with lipopolysaccaride (LPS) and thereby to increase the amount of cell surface receptors was assessed by flow cytometry and reverse transcription-polymerase chain reaction (RT-PCR). The results showed that PCL fibres did not inhibit this function compared to TCP. As-spun PCL fibres were loaded with 1 % ovine albumin (OVA) powder, 1% OVA nanoparticles and 5% OVA nanoparticles by weight and the protein release was assessed in vitro. PCL fibres loaded with 1 % OVA powder released 70%, 1% OVA nanoparticle released 60% and the 5% OVA nanoparticle released 25% of their protein content over 28 days. These release figures did not alter when the fibres were subjected to lipase enzymatic degradation. The OVA released was examined for structural integrity by SDS-PAGE. This showed that the protein molecular weight was not altered after incorporation into the fibres. The bioactivity of progesterone was assessed following incorporation into PCL fibres. Results showed that the progesterone released had a pronounced effect on MCF-7 breast epithelial cells, inhibiting their proliferation. The PCL fibres display high fibre compliance, a potential for controlling the fibre surface architecture to promote contact guidance effects, favorable proliferation rate of fibroblasts, myoblasts and HUVECs and the ability to release pharmaceuticals. These properties recommended their use for 3-D scaffold production in soft tissue engineering and the fibres could also be exploited for controlled presentation and release of biopharmaceuticals such as growth factors.

Tissue engineering of co-cultured skin substitutes using biocomposite membranes based on collagen and polycaprolactone

The preparation and characterisation of collagen: PCL, gelatin: PCL and gelatin/collagen:PCL biocomposites for manufacture of tissue engineered skin substitutes are reported. Films of collagen: PLC, gelatin: PCL (1:4, 1:8 and 1:20 w/w) and gelatin/collagen:PCL (1:8 and 1:20 w/w) biocomposites were prepared by impregnation of lyophilised collagen and/or gelatin mats by PCL solutions followed by solvent evaporation. In vitro assays of total protein release of collagen:PCL and gelatin: PCL biocomposite films revealed an expected inverse relationship between the collagen release rate and the content of synthetic polymer in the biocomposite samples that may be exploited for controlled presentation and release of biopharmaceuticals such as growth factors. Good compatibility of all biocomposite groups was proven by interaction with 3T3 fibroblasts, normal human epidermal keratinocytes (NHEK), and primary human epidermal keratinocytes (PHEK) and dermal fibroblasts (PHDF) in vitro respectively. The 1:20 collagen: PCL materials exhibiting good cell growth curves and mechanical characteristics were selected for engineering of skin substitutes in this work. The tissue-engineered skin model based on single-donor PHEK and PHDF with differentiated confluent epidermal layer and fibrous porous dermal layer was then developed successfully in vitro proven by SEM and immunohistochemistry assay. The following in vivo animal study on athymic mice revealed early complete wound healing in 10 days and good integration of co-cultured skin substitutes with adjacent mice skin structures. Thus the co-cultured skin substitutes based on 1:20 collagen: PCL biocomposite membranes was proven in principle. The approach to skin modelling reported here may find application in wound treatment, gene therapy and screening of new pharmaceuticals.

Decellularization of bovine corneas for tissue engineering applications

Scaffolds derived from processed tissues offer viable alternatives to synthetic polymers as biological scaffolds for regenerative medicine. Tissue-derived scaffolds provide an extracellular matrix (ECM) as the starting material for wound healing and the functional reconstruction of tissues, offering a potentially valuable approach for the replacement of damaged or missing tissues. Additionally, acellular tissue may provide a natural microenvironment for host-cell migration and the induction of stem cell differentiation to contribute to tissue regeneration. There are a number of processing methods that aim to stabilize and provide an immunologically inert tissue scaffold. Furthermore, these tissue-processing methods can often be applied to xenogenic transplants because the essential components of the ECM are often maintained between species. In this study, we applied several tissue-processing protocols to the cornea in order to obtain a decellularized cornea matrix that maintained the clarity and mechanical properties of the native tissue. Histology, mechanical testing and electron microscopy techniques were used to assess the cell extraction process and the organization of the remaining ECM. In vitro cell seeding experiments confirmed the processed corneas’ biocompatibility.

Composite cell support membranes based on collagen and polycaprolactone for tissue engineering of skin

The preparation and characterisation of collagen:PCL composites for manufacture of tissue engineered skin substitutes and models are reported. Films having collagen:PCL (w/w) ratios of 1:4, 1:8 and 1:20 were prepared by impregnation of lyophilised collagen mats by PCL solutions followed by solvent evaporation. In vitro assays of collagen release and residual collagen content revealed an expected inverse relationship between the collagen release rate and the content of synthetic polymer in the composite that may be exploited for controlled presentation and release of biopharmaceuticals such as growth factors. DSC analysis revealed the characteristic melting point of PCL at around 60°C and a tendency for the collagen component, at high loading, to impede crystallinity development within the PCL phase. The preparation of fibroblast/composite constructs was investigated using cell culture as a first stage in mimicking the dermal/epidermal structure of skin. Fibroblasts were found to attach and proliferate on all the composites investigated reaching a maximum of 2×105/cm2 on 1:20 collagen:PCL materials at day 8 with cell numbers declining thereafter. Keratinocyte growth rates were similar on all types of collagen:PCL materials investigated reaching a maximum of 6.6×104/cm2 at day 6. The results revealed that composite films of collagen and PCL are favourable substrates for growth of fibroblasts and keratinocytes and may find utility for skin repair. © 2003 Elsevier Ltd. All rights reserved.

Gravity spun polycaprolactone fibres for soft tissue engineering:interaction with fibroblasts and myoblasts in cell culture

Poly(ε-caprolactone) (PCL) fibres were produced by wet spinning from solutions in acetone under low shear (gravity flow) conditions. As-spun PCL fibres exhibited a mean strength and stiffness of 7.9 MPa and 0.1 GPa, respectively and a rough, porous surface morphology. Cold drawing to an extension of 500% resulted in increases in fibre strength (43 MPa) and stiffness (0.3 GPa) and development of an oriented, fibrillar surface texture. The proliferation rate of Swiss 3T3 mouse fibroblasts and C2C12 mouse myoblasts on as-spun, 500% cold-drawn and gelatin-modified PCL fibres was determined in cell culture to provide a basic measure of the biocompatibility of the fibres. Proliferation of both cell types was consistently higher on gelatin-coated fibres relative to as-spun fibres at time points below 7 days. Fibroblast growth rates on cold-drawn PCL fibres exceeded those on as-spun fibres but myoblast proliferation was similar on both substrates. After 1 day in culture, both cell types had spread and coalesced on the fibres to form a cell layer, which conformed closely to the underlying topography. The high fibre compliance combined with a potential for modifying the fibre surface chemistry with cell adhesion molecules and the surface architecture by cold drawing to enhance proliferation of fibroblasts and myoblasts, recommends further investigation of gravity-spun PCL fibres for 3-D scaffold production in soft tissue engineering. © 2005 Elsevier Ltd. All rights reserved.

Atmospheric plasma treatment of porous polymer constructs for tissue engineering applications

Porous 3D polymer scaffolds prepared by TIPS from PLGA (53:47) and PS are intrinsically hydrophobic which prohibits the wetting of such porous media by water. This limits the application of these materials for the fabrication of scaffolds as supports for cell adhesion/spreading. Here we demonstrate that the interior surfaces of polymer scaffolds can be effectively modified using atmospheric air plasma (AP). Polymer films (2D) were also modified as control. The surface properties of wet 2D and 3D scaffolds were characterised using zeta-potential and wettability measurements. These techniques were used as the primary screening methods to assess surface chemistry and the wettability of wet polymer constructs prior and after the surface treatment. The surfaces of the original polymers are rather hydrophobic as highlighted but contain acidic functional groups. Increased exposure to AP improved the water wetting of the treated surfaces because of the formation of a variety of oxygen and nitrogen containing functions. The morphology and pore structure was assessed using SEM and a liquid displacement test. The PLGA and PS foam samples have central regions which are open porous interconnected networks with maximum pore diameters of 49 μm for PLGA and 73 μm for PS foams. (Figure Presented) © 2007 Wiley-VCH Verlag GmbH & Co. KGaA.

The early career researcher's toolkit:translating tissue engineering, regenerative medicine and cell therapy products

Although the importance of translation for the development of tissue engineering, regenerative medicine and cell-based therapies is widely recognized, the process of translation is less well understood. This is particularly the case among some early career researchers who may not appreciate the intricacies of translational research or make decisions early in development which later hinders effective translation. Based on our own research and experiences as early career researchers involved in tissue engineering and regenerative medicine translation, we discuss common pitfalls associated with translational research, providing practical solutions and important considerations which will aid process and product development. Suggestions range from effective project management, consideration of key manufacturing, clinical and regulatory matters and means of exploiting research for successful commercialization.

Microporous polycaprolactone matrices for drug delivery and tissue engineering:the release behaviour of bioactives having extremes of aqueous solubility

Microporous polycaprolactone (PCL) matrices loaded with hydrophobic steroidal drugs or a hydrophilic drug - pilocarpine hydrochloride - were produced by precipitation casting using solutions of PCL in acetone. The efficiency of steroid incorporation in the final matrix (progesterone (56 %) testosterone (46 %) dexamethasone (80 %)) depended on the nature of the drug initially co-dissolved in the PCL solution. Approximately 90 % w/w of the initial load of progesterone, 85 % testosterone and 50 % dexamethasone was released from the matrices in PBS at 37°C over 8 days. Pilocarpine hydrochloride (PH)-loaded PCL matrices, prepared by dispersion of powder in PCL solution, released 70-90 % of the PH content over 12 days in PBS. Application of the Higuchi model revealed that the kinetics of steroid and PH release were consistent with a Fickian diffusion mechanism with corresponding diffusion coefficients of 5.8 × 10-9 (progesterone), 3.9 × 10 -9 (testosterone), 7.1 × 10-10 (dexamethasone) and 22 × 10-8 cm2/s (pilocarpine hydrochloride). The formulation techniques described are expected to be useful for production of implantable, insertable and topical devices for sustained delivery of a range of bioactive molecules of interest in drug delivery and tissue engineering.

3D culture of bone-derived cells immobilised in alginate following light-triggered gelation

Photoreactive liposomes have been exploited as a means of developing 3D tissue constructs. Liposomes formulated using the photosensitive lipid 1,2-bis(4-(n-butyl)phenylazo-4′-phenylbutyroyl)phosphatidylcholine (Bis Azo PC), which undergoes conformational change on stimulation with long wavelength ultraviolet light, were prepared with entrapped CaCl2 before being incorporated into a 4% alginate solution. It was shown that stimulation of the photosensitive lipid using a light emitting diode (LED) (peak emission at 385 nm, dose equivalent to 9 mJ/cm2) caused the release of liposome-entrapped CaCl2, resulting in cross-linking of the alginate solution and immobilisation of bone-derived cells over a range of seeding densities, approximately 97% of which remained viable for periods of up to 14 days in culture. Entrapment volumes of a variety of liposome types were evaluated and interdigitating fusion vesicles were identified as having the highest payload (24%), however the inclusion of cholesterol as a means of shifting Bis Azo PC sensitivity into the visible light wavelengths resulted in an approximately 10-fold reduction in calcium entrapment. This application of light-sensitised liposomes offers the potential to create complex tissue engineering substrates containing cells immobilised in precise locations, in contrast with substrates onto which cells are seeded post-production. © 2007 Elsevier B.V. All rights reserved.

Measuring the dynamic mechanical response of hydrated mouse bone by nanoindentation

This study demonstrates a novel approach to characterizing hydrated bone's viscoelastic behavior at lamellar length scales using dynamic indentation techniques. We studied the submicron-level viscoelastic response of bone tissue from two different inbred mouse strains, A/J and B6, with known differences in whole bone and tissue-level mechanical properties. Our results show that bone having a higher collagen content or a lower mineral-to-matrix ratio demonstrates a trend towards a larger viscoelastic response. When normalized for anatomical location relative to biological growth patterns in the antero-medial (AM) cortex, bone tissue from B6 femora, known to have a lower mineral-to-matrix ratio, is shown to exhibit a significantly higher viscoelastic response compared to A/J tissue. Newer bone regions with a higher collagen content (closer to the endosteal edge of the AM cortex) showed a trend towards a larger viscoelastic response. Our study demonstrates the feasibility of this technique for analyzing local composition-property relationships in bone. Further, this technique of viscoelastic nanoindentation mapping of the bone surface at these submicron length scales is shown to be highly advantageous in studying subsurface features, such as porosity, of wet hydrated biological specimens, which are difficult to identify using other methods. © 2010 Elsevier Ltd.

A biological-inspired support frame for an artificial cornea

Bilateral corneal blindness represents a quarter of the total blind, world-wide. The artificial cornea in assorted forms, was developed to replace opaque non-functional corneas and to return sight in otherwise hopeless cases that were not amenable to corneal grafts; believed to be 2% of corneal blind. Despite technological advances in materials design and tissue engineering no artificial cornea has provided absolute, long-term success. Formidable problems exist, due to a combination of unpredictable wound healing and unmanageable pathology. To have a solid guarantee of reliable success an artificial cornea must possess three attributes: an optical window to replace the opaque cornea; a strong, long term union to surrounding ocular tissue; and the ability to induce desired host responses. A unique artificial cornea possesses all three functional attributes- the Osteo-odonto-keratoprosthesis (OOKP). The OOKP has a high success rate and can survive for up to twenty years, but it is complicated both in structure and in surgical procedure; it is expensive and not universally available. The aim of this project was to develop a synthetic substitute for the OOKP, based upon key features of the tooth and bone structure. In doing so, surgical complexity and biological complications would be reduced. Analysis of the biological effectiveness of the OOKP showed that the structure of bone was the most crucial component for implant retention. An experimental semi-rigid hydroxyapatite framework was fabricated with a complex bone-like architecture, which could be fused to the optical window. The first method for making such a framework, was pressing and sintering of hydroxyapatite powders; however, it was not possible to fabricate a void architecture with the correct sizes and uniformity of pores. Ceramers were synthesised using alternative pore forming methods, providing for improved mechanical properties and stronger attachment to the plastic optical window. Naturally occurring skeletal structures closely match the structural features of all forms of natural bone. Synthetic casts were fabricated using the replamineform process, of desirable natural artifacts, such as coral and sponges. The final method of construction by-passed ceramic fabrication in favour of pre-formed coral derivatives and focused on methods for polymer infiltration, adhesion and fabrication. Prototypes were constructed and evaluated; a fully penetrative synthetic OOKP analogue was fabricated according to the dimensions of the OOKP. Fabrication of the cornea shaped OOKP synthetic analogue was also attempted.